Creep and residual properties of filament-wound composite rings under radial compression in harsh environments
Visualizar/abrir
Data
2021Autor
Tipo
Assunto
Abstract
This work focuses on the viscoelastic response of carbon/epoxy filament-wound composite rings under radial compressive loading in harsh environments. The composites are exposed to three hygro-thermo-mechanical conditions: (i) pure mechanical loading, (ii) mechanical loading in a wet environment and (iii) mechanical loading under hygrothermal conditioning at 40 ◦C. Dedicated equipment was built to carry out the creep experiments. Quasi-static mechanical tests are performed before and after creep ...
This work focuses on the viscoelastic response of carbon/epoxy filament-wound composite rings under radial compressive loading in harsh environments. The composites are exposed to three hygro-thermo-mechanical conditions: (i) pure mechanical loading, (ii) mechanical loading in a wet environment and (iii) mechanical loading under hygrothermal conditioning at 40 ◦C. Dedicated equipment was built to carry out the creep experiments. Quasi-static mechanical tests are performed before and after creep tests to evaluate the residual properties of the rings. The samples are tested in (i) radial compression, (ii) axial compression, and (iii) hoop tensile strength. Different laminates wound at off-axis orientations are manufactured via filament winding and analyzed. Key results show that creep displacement is affected by both hygrothermal and mechanical conditionings, especially at a higher temperature. Moreover, residual properties are quantified showing that creep generates permanent damage in the cylinders. ...
Contido em
Polymers [recurso eletrônico]. Basel. Vol. 13, n. 1 (2021), [Article] 33, p. 1-18
Origem
Estrangeiro
Coleções
-
Artigos de Periódicos (39351)Engenharias (2404)
Este item está licenciado na Creative Commons License
![](/themes/Mirage2Novo//images/lume/cc.png)