Thermal stability and diffusion in gadolinium silicate gate dielectric films
![Thumbnail](/bitstream/handle/10183/141228/000308419.pdf.jpg?sequence=3&isAllowed=y)
Visualizar/abrir
Data
2001Autor
Tipo
Assunto
Abstract
Gadolinium silicate films on Si(100) annealed in oxygen and vacuum at temperatures up to 800 °C were analyzed by Rutherford backscattering and narrow resonance nuclear profiling. Oxygen diffused into the film eliminating oxygen vacancies, but Si diffusion, previously observed in Al and Y oxides and in La and Zr silicate films, was absent. Higher-temperature annealing in oxygen resulted in the formation of an interfacial layer observable in high-resolution electron micrographs. Gd0.23Si0.14O0.63 ...
Gadolinium silicate films on Si(100) annealed in oxygen and vacuum at temperatures up to 800 °C were analyzed by Rutherford backscattering and narrow resonance nuclear profiling. Oxygen diffused into the film eliminating oxygen vacancies, but Si diffusion, previously observed in Al and Y oxides and in La and Zr silicate films, was absent. Higher-temperature annealing in oxygen resulted in the formation of an interfacial layer observable in high-resolution electron micrographs. Gd0.23Si0.14O0.63 films crystallize at temperatures between 1000 and 1050 °C. These observations combined with recent electrical measurements show that gadolinium silicate films may be a good candidate for the replacement of SiO2 in deep submicron metal–oxide–semiconductor gates. ...
Contido em
Applied physics letters. Melville. Vol. 79, no. 16 (Oct. 2001), p. 2618-2620
Origem
Estrangeiro
Coleções
-
Artigos de Periódicos (39351)Ciências Exatas e da Terra (5974)
Este item está licenciado na Creative Commons License
![](/themes/Mirage2Novo//images/lume/cc.png)